Complete wax conversion Chart:
Click here to view and print the complete Wax Conversion Chart
Formula
Pattern Wax Weight(g) X Density of Alloy (g/cm³) ÷ 1.5 = Weight of Alloy in (dwts) needed for casting
Conversions
To convert grams to dwts: Multiply by 0.64301
To convert dwts to grams: Multiply by 1.555
Porcelain Alloys
| Alloy Name | Density (g/cm³) |
0.10 | 0.20 | 0.30 | 0.40 | 0.50 | 0.60 | 0.70 | 0.80 | 0.90 | 1.00 | 2.00 | 3.00 |
| Amount of Alloy Needed (dwts) | |||||||||||||
| Aztec | 19.3 | 1.3 | 2.5 | 3.8 | 5.0 | 6.2 | 7.5 | 8.7 | 9.9 | 11.2 | 12.4 | 24.8 | 37.1 |
| Classic IV | 19.0 | 1.3 | 2.5 | 3.8 | 5.1 | 6.3 | 7.6 | 8.9 | 10.1 | 11.4 | 12.7 | 25.3 | 38.0 |
| JP-II | 18.5 | 1.2 | 2.5 | 3.7 | 4.9 | 6.2 | 7.4 | 8.6 | 9.9 | 11.1 | 12.3 | 24.7 | 37.0 |
| PREMIERE | 18.8 | 1.3 | 2.5 | 3.8 | 5.0 | 6.3 | 7.5 | 8.8 | 10.0 | 11.3 | 12.5 | 25.1 | 37.6 |
| ENDURANCE | 18.2 | 1.2 | 2.4 | 3.6 | 4.9 | 6.1 | 7.3 | 8.5 | 9.7 | 10.9 | 12.1 | 24.3 | 36.4 |
| JP-80 | 16.0 | 1.1 | 2.1 | 3.2 | 4.3 | 5.3 | 6.4 | 7.5 | 8.5 | 9.6 | 10.7 | 21.3 | 32.0 |
| OVERTURE | 16.6 | 1.1 | 2.2 | 3.3 | 4.4 | 5.5 | 6.6 | 7.7 | 8.9 | 10.0 | 11.1 | 22.1 | 33.2 |
| EQUITY | 15.4 | 1.0 | 2.2 | 3.1 | 4.1 | 5.1 | 6.2 | 7.2 | 8.2 | 9.2 | 10.3 | 20.5 | 30.8 |
| SENTRY | 14.4 | 1.0 | 1.9 | 2.9 | 3.8 | 4.8 | 5.8 | 6.7 | 7.7 | 8.6 | 9.6 | 19.2 | 28.8 |
| FOUNDATION | 13.9 | 0.9 | 1.9 | 2.8 | 3.7 | 4.6 | 5.6 | 6.5 | 7.4 | 8.3 | 9.3 | 18.5 | 27.8 |
| JP-I | 14.0 | 0.9 | 1.9 | 2.8 | 3.7 | 4.7 | 5.6 | 6.5 | 7.5 | 8.4 | 9.3 | 18.7 | 28.0 |
| JPW | 13.6 | 0.9 | 1.8 | 2.7 | 3.6 | 4.5 | 5.4 | 6.3 | 7.3 | 8.2 | 9.1 | 18.1 | 27.2 |
| JP-I-A | 13.6 | 0.9 | 1.8 | 2.7 | 3.6 | 4.5 | 5.4 | 6.3 | 7.3 | 8.2 | 9.1 | 18.1 | 27.2 |
| VERITY | 13.8 | 0.9 | 1.8 | 2.8 | 3.7 | 4.6 | 5.5 | 6.4 | 7.4 | 8.3 | 9.2 | 18.4 | 27.6 |
| SECURITY | 13.0 | 0.9 | 1.7 | 2.6 | 3.5 | 4.3 | 5.2 | 6.1 | 6.9 | 7.8 | 8.7 | 17.3 | 26.0 |
| PULSE N3 | 11.5 | 0.8 | 1.5 | 2.3 | 3.0 | 3.9 | 4.5 | 5.2 | 6.0 | 6.7 | 7.4 | 14.8 | 22.1 |
| INTEGRITY | 10.9 | 0.7 | 1.5 | 2.2 | 2.9 | 3.6 | 4.4 | 5.1 | 5.8 | 6.5 | 7.3 | 14.5 | 21.8 |
| STABILITY | 10.7 | 0.7 | 1.4 | 2.1 | 2.9 | 3.6 | 4.3 | 5.0 | 5.7 | 6.4 | 7.1 | 14.3 | 21.4 |
| ADVANTAGE | 10.7 | 0.7 | 1.4 | 2.1 | 2.9 | 3.6 | 4.3 | 5.0 | 5.7 | 6.4 | 7.1 | 14.3 | 21.4 |
| SOLUTION | 10.7 | 0.7 | 1.4 | 2.1 | 2.9 | 3.6 | 4.3 | 5.0 | 5.7 | 6.4 | 7.1 | 14.3 | 21.4 |
| SUPERIOR | 11.0 | 0.7 | 1.5 | 2.2 | 2.9 | 3.7 | 4.4 | 5.1 | 5.9 | 6.6 | 7.3 | 14.7 | 22.0 |
| SUPERIOR PLUS | 11.1 | 0.7 | 1.5 | 2.2 | 3.0 | 3.7 | 4.4 | 5.2 | 5.9 | 6.7 | 7.4 | 14.8 | 22.2 |
| JP-5 | 11.0 | 0.7 | 1.5 | 2.2 | 2.9 | 3.7 | 4.4 | 5.1 | 5.9 | 6.6 | 7.3 | 14.7 | 22.0 |
| JP5 w/Au | 11.0 | 0.7 | 1.5 | 2.2 | 2.9 | 3.7 | 4.4 | 5.1 | 5.9 | 6.6 | 7.3 | 14.7 | 22.0 |
Crown and Bridge Alloys
| Alloy Name | Density (g/cm³) | 0.10 | 0.20 | 0.30 | 0.40 | 0.50 | 0.60 | 0.70 | 0.80 | 0.90 | 1.00 | 2.00 | 3.00 |
| Amount of Alloy Needed (dwts) | |||||||||||||
| JA | 16.4 | 1.1 | 2.2 | 3.3 | 4.4 | 5.5 | 6.6 | 7.7 | 8.7 | 9.8 | 10.9 | 21.9 | 32.8 |
| JRVT | 15.4 | 1.0 | 2.1 | 3.1 | 4.1 | 5.1 | 6.2 | 7.2 | 8.2 | 9.2 | 10.3 | 20.5 | 30.8 |
| JRVT-PF | 15.4 | 1.0 | 2.1 | 3.1 | 4.1 | 5.1 | 6.2 | 7.2 | 8.2 | 9.2 | 10.3 | 20.5 | 30.8 |
| JB | 15.4 | 1.0 | 2.1 | 3.1 | 4.1 | 5.1 | 6.2 | 7.2 | 8.2 | 9.2 | 10.3 | 20.5 | 30.8 |
| JC | 15.2 | 1.0 | 2.0 | 3.0 | 4.1 | 5.1 | 6.1 | 7.1 | 8.1 | 9.1 | 10.1 | 20.3 | 30.4 |
| JIV PF | 15.9 | 1.1 | 2.1 | 3.1 | 4.1 | 5.3 | 6.4 | 7.4 | 8.5 | 9.5 | 10.6 | 21.2 | 31.8 |
| JIV | 14.5 | 1.0 | 1.9 | 2.9 | 3.9 | 4.8 | 5.8 | 6.8 | 7.7 | 8.7 | 9.7 | 19.3 | 29.0 |
| JCB | 14.2 | 0.9 | 1.9 | 2.8 | 3.8 | 4.7 | 5.7 | 6.6 | 7.6 | 8.5 | 9.5 | 18.9 | 28.4 |
| JCBD | 13.5 | 0.9 | 1.8 | 2.7 | 3.6 | 4.5 | 5.4 | 6.3 | 7.2 | 8.1 | 9.0 | 18.0 | 27.0 |
| JLCB | 13.7 | 0.9 | 1.8 | 2.7 | 3.7 | 4.6 | 5.5 | 6.4 | 7.3 | 8.2 | 9.1 | 18.3 | 27.4 |
| State | 12.5 | 0.8 | 1.7 | 2.5 | 3.4 | 4.2 | 5.0 | 5.9 | 6.7 | 7.6 | 8.4 | 16.8 | 25.2 |
| JYE | 12.8 | 0.9 | 1.7 | 2.6 | 3.4 | 4.3 | 5.1 | 6.0 | 6.8 | 7.7 | 8.5 | 17.1 | 25.6 |
| J-3 | 12.9 | 0.9 | 1.1 | 2.6 | 3.4 | 4.3 | 5.2 | 6.0 | 6.9 | 7.7 | 8.6 | 17.2 | 25.8 |
| JMC | 12.9 | 0.9 | 1.7 | 2.6 | 3.4 | 4.3 | 5.2 | 6.0 | 6.9 | 7.7 | 8.6 | 17.2 | 25.8 |
| SL-40 | 12.7 | 0.8 | 1.7 | 2.5 | 3.4 | 4.2 | 5.1 | 5.9 | 6.8 | 7.6 | 8.5 | 16.9 | 25.4 |
| CASTELL | 11.0 | 0.7 | 1.5 | 2.2 | 2.9 | 3.7 | 4.4 | 5.1 | 5.9 | 6.6 | 7.3 | 14.7 | 22.0 |
| Blaze | 10.3 | 0.7 | 1.4 | 2.1 | 2.7 | 3.4 | 4.1 | 4.8 | 5.5 | 6.2 | 6.9 | 13.7 | 21.0 |
| JWG | 10.6 | 0.7 | 1.4 | 2.1 | 2.8 | 3.5 | 4.2 | 4.9 | 5.7 | 6.4 | 7.1 | 14.1 | 21.2 |
| JWE | 10.6 | 0.7 | 1.4 | 2.1 | 2.8 | 3.5 | 4.2 | 4.9 | 5.7 | 6.4 | 7.1 | 14.1 | 21.2 |
| J-7 | 10.1 | 0.7 | 1.3 | 2.0 | 2.7 | 3.4 | 4.0 | 4.7 | 5.4 | 6.1 | 6.7 | 13.5 | 20.2 |
Universal Alloys
| Alloy Name | Density (g/cm³) |
0.10 | 0.20 | 0.30 | 0.40 | 0.50 | 0.60 | 0.70 | 0.80 | 0.90 | 1.00 | 2.00 | 3.0 |
| Amount of Alloy Needed (dwts) | |||||||||||||
| Galileo | 16.4 | 1.1 | 2.1 | 3.2 | 4.2 | 5.3 | 6.3 | 7.4 | 8.4 | 9.5 | 10.5 | 20.1 | 31.5 |
| Galileo-PF | 16.9 | 1.1 | 2.2 | 3.3 | 4.4 | 5.5 | 6.5 | 7.6 | 8.7 | 9.8 | 10.9 | 21.7 | 32.5 |